vol.58 número1DISPLACEMENT-DISPERSIVE LIQUID-LIQUID MICROEXTRACTION BASED ON SOLIDIFICATION FLOATING ORGANIC DROP TRACE AMOUNTS OF LEAD IN WATER SAMPLE PRIOR TO FLAME ATOMIC ABSORPTION SPECTROMETRY DETERMINATIONNANOPARTICLES DISPERSION IN PROCESSING NANOSTRUCTURE CHIRAL POLY(AMIDE-IMIDE)S BASED ON 7V-TRIMELLITYLIMIDO-Z,-LEUCINE/TiO2 NANOCOMPOSITES: ALLOCATION AND PROPERTIES índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

Compartilhar


Journal of the Chilean Chemical Society

versão On-line ISSN 0717-9707

Resumo

POOLEY, S.AMALIA; RIVAS, BERNABÉ L  e  PIZARRO, GUADALUPE DEL C. HYDROGELS BASED ON (DIMETHYLAMINO)ETHYLACRYLATE (DMAEA) AND N,N'-DIMETHYLACRYLAMIDE (NNDMAAM): SYNTHESIS, CHARACTERIZATION, AND SWELLING BEHAVIOR. J. Chil. Chem. Soc. [online]. 2013, vol.58, n.1, pp.1597-1602. ISSN 0717-9707.  http://dx.doi.org/10.4067/S0717-97072013000100021.

Hydrogels of 2-(dimethylamino)ethylacrylate (DMAEA) with N,N'-dimethyl acrylamide (NNDMAAm) were synthesized by solution free-radical polymerization at different feed mol ratios. These copolymers were completely water-insoluble. Polymers were characterized by elemental analysis, FT-IR spectroscopy, thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). The monomer reactivity ratios were determined by Kelen-Tüdos method. According to that, the monomer reactivity ratios for poly(DMAEA-co-NNDMAAm) were r1 = 0.288 (M1=DMAEA) and r2 = 1.460 (M2=NNDMAAm), (r1x r 2 = 0.419). Low critical solution temperatures (LCST) values of hydrogels are around 60°C, which was significantly higher than that poly(NIPAAm) and increased with increasing of hydrophilic DMAEA unit content in the copolymers. The hydrogels achieved a water-absorption value of 188 g of water/g of dry polymer (xerogel) in distilled water. Effects of time, temperature, pH, salt concentration, cross-linking concentration, and solvent polarity on the water absorption were studied. Experimental results indicated that the copolymer poly(DMAEA-co-NNDMAAm) with a feed mol ratio 2:1 presents the best swelling properties.

Palavras-chave : Hydrogels; radical polymerization; swelling; stimuli-sensitive polymers.