SciELO - Scientific Electronic Library Online

 
vol.16 número4El Ensayo de Punzonado en Caliente Aplicado a un Acero Microaleado con NiobioComportamiento Frente a la Corrosión en Ambiente Marino de Acero Galvanizado y Acero Galvanizado Pintado (Duplex) índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Información tecnológica

versión On-line ISSN 0718-0764

Resumen

HURTADO, E.; GARNICA, P.  y  LOPEZ, A.. Use of the Roundness Parameter to Evaluate Intergranular Cavitation of Low Carbon Niobium Microalloyed Steel under Isothermal Deformation. Inf. tecnol. [online]. 2005, vol.16, n.4, pp.45-51. ISSN 0718-0764.  http://dx.doi.org/10.4067/S0718-07642005000400008.

Hot tensile tests were carried out on low-carbon niobium microalloyed steel at four temperatures: 640°C, 840°C, 900°C and 960°C, for  crosshead speeds of 1.35 mm/min and 13.5 mm/min in order to evaluate cavity formation behavior during isothermic deformation. After fracture in a hot tensile test,  transverse sample sectioning allowed the evaluation of shape and size of cavities formed during the test using optical microscopy and image analysis. In both cases zigzag shaped cavities were observed at 900°C, a temperature within the range of the lowest ductility for this steel under uniaxial tensile load conditions. It was found that cavities formed at 1.35 mm/min  at this temperature were greater in size, and had a lower relative value for the roundness parameter.

Palabras clave : intergranular cavitation; isothermal deformation; cavity nucleation; roundness parameter.