SciELO - Scientific Electronic Library Online

 
vol.26 número5Propiedades Fisicoquímicas y de Flujo de un Yogur Asentado Enriquecido con Microcápsulas que Contienen Ácidos Grasos Omega 3Propiedades Volumétricas de Trifluorometanosulfonato de 1-etil-3-metilimidazolio en Solución acuosa de Tiosulfato de Sodio Pentahidratado a Diferentes Temperaturas índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Información tecnológica

versão On-line ISSN 0718-0764

Resumo

REALPE, Álvaro; MENDEZ, Nayilis; TOSCANO, Eduardo  e  ACEVEDO, María T. Synthesis and Physicochemical Characterization of a Membrane Loaded with TiO2 Prepared from sulfonation of a Copolymer of Acrylic Ester and Styrene. Inf. tecnol. [online]. 2015, vol.26, n.5, pp.97-104. ISSN 0718-0764.  http://dx.doi.org/10.4067/S0718-07642015000500013.

Proton exchange membranes were prepared from a copolymer of acrylic ester and styrene, and their physicochemical properties were investigated for application in fuel cells. The properties of the membrane were modified from the sulfonation reaction and addition of titanium dioxide (TiO2). Physicochemical characterization of water uptake, ion exchange capacity and thermal analysis were carried out to the membranes prepared. The sulfonated-loaded membrane (SC) presented ion exchange capacity of 0.27 meq/g, water uptake of 25.8% and tensile strength of 4.63 MPa. These results confirm that the introduction of sulfonic groups and TiO2 addiction improve the physiochemical properties of the unmodified membrane, indicating that the prepared membranes have potential for applications in proton exchange fuel cells.

Palavras-chave : copolymer of acrylic ester; styrene; polymeric membrane; proton exchange.