SciELO - Scientific Electronic Library Online

 
vol.27 número6Encapsulación de Alimentos Probióticos mediante Liofilización en Presencia de PrebióticosSintesis y Caracterización del Nanomaterial TiO2-MWCNTs (Oxido de Titanio-Nanotubos de Carbono de Pared Múltiple) índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Información tecnológica

versión On-line ISSN 0718-0764

Resumen

DELGADO, Karen L; VARONA, Giovanni A; MONTILLA, Camilo E  y  VILLADA, Héctor S. Effect of the Additive Tween 80 and of the Process Temperature on the Mechanical Tensile Properties of Flexible Films Developed from Thermoplastic Cassava Starch. Inf. tecnol. [online]. 2016, vol.27, n.6, pp.145-152. ISSN 0718-0764.  http://dx.doi.org/10.4067/S0718-07642016000600015.

The aim of this research was to evaluate the effect of processing temperature and concentration of the additive Tween 80 on the mechanical tensile properties of a flexible film made of cassava thermoplastic starch (TPS), polylactic acid (PLA) and polycaprolactone (PCL). An experimental design was carried out to determine the temperature profile and Tween 80 concentration. Thereafter, treatment was chosen with the most outstanding results in mechanical properties and compared with a standard film (without Tween 80). The outstanding values of tensile strength (6.13 MPa), elongation (82.83%), and modulus of elasticity (243.06 MPa) were obtained with a concentration of 0.75% and temperature profile of 137.35 ° C. It is concluded that the addition of Tween 80 did not significantly affect the properties studied of the flexible films.

Palabras clave : thermoplastic starch (TPS); polylactic acid (PLA); polycaprolactone (PCL); Tween 80; flexible film.