SciELO - Scientific Electronic Library Online

 
vol.28 número6Remoción de Arsénico (V) en Solución Acuosa por Biomasa Modificada del Hongo AspergiHus nigerRelación de Capacitación con Adopción de Internet y E-Commerce: Diferencias entre Microemprendedores de Chile índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Información tecnológica

versión On-line ISSN 0718-0764

Resumen

GONZALEZ, Rafael E; TARON, Arnulfo  y  PEREZ, Jaime. Biofilms of Gellan Loaded with Silver Nanoparticles: Physico Mechanical, Antimicrobials and Barrier Properties. Inf. tecnol. [online]. 2017, vol.28, n.6, pp.53-60. ISSN 0718-0764.  http://dx.doi.org/10.4067/S0718-07642017000600007.

Biofilms based on low acyl gellan loaded with silver nanoparticles (AgNPs) were tested, evaluating their physical-mechanical, antimicrobial and barrier properties after 3 weeks of storage. The antimicrobial activity was evaluated against food-borne bacteria (Escherichia coli and Staphylococcus aureus) and two fungi (Aspergillus sp and Penicillium sp). The results showed that the storage time influence all the evaluated properties. Increasing the storage time decreases the tensile strength and transparency values. Also, the antimicrobial power and the water vapor permeability increased. This behavior is probably due to the leaching of silver ions, which decreases the number of bonds present in the polymer matrix. Such results are promising and suggest the possibility of using biofilms based on low acyl gellan as a system for the vehiculation of AgNPs for their gradual release while maintaining a sustained antimicrobial effect.

Palabras clave : biofilms; gellan gum; silver nanoparticles; permeability; tensile strength.