vol.14 número2Efecto de la densidad de plantación inicial en el módulo de elasticidad dinámico de árboles en pie y trozas de una plantación de pino radiata de 28 años, en la zona de arenales, ChileEffect of thermal rectification on colors of Eucalyptus Saligna and Pinus caribaea Woods índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

Compartilhar


Maderas. Ciencia y tecnología

versão On-line ISSN 0718-221X

Resumo

VALENZUELA C, Paulina; BUSTOS A, Cecilia; LASSERRE, Jean Pierre  e  GACITUA E, William. Fracture in Eucalyptus nitens wood: effect of nanomechanical properties, ultrastructure and anatomical level . Maderas, Cienc. tecnol. [online]. 2012, vol.14, n.2, pp.225-238. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2012000200009.

This study was conducted to investigate the causes and posibles factors related to fractures in the cellular structure in Eucalyptus nitens. Nanomechanical cell wall properties at the middle lamella level (ML), S1 and S2 layers were evaluated. In addition, the area, and diameter of vessels were measured. These parameters were associated with extreme levels of cracking (high and low) in two Eucalyptus nitens families. The samples were taked from two sites of the 8th Region of Chile. The analysis of the ductility ratio (E/H) demonstrated that the ML is more brittle than the S1 layer; and the S1 is more brittle than S2 layer. The ML and S1 layer behave like resilient materials, but not the S2 layer. The difference in the modulus of resilience was related to higher shear stresses at the ML/S2 and at S1/S2 interfaces. The characterization of the vessels showed that the families with greater level of cracking have also lower frequency and greater area and diameter of vessels The S1 layer was weaker tan S2 layer and LM due to their difference in resistance between them and combined with the internal stresses might propagate the microcracks.

Palavras-chave : Eucalyptus nitens; nanoindentations; nanomechanical properties; wood anatomy; wood cell fracture.