SciELO - Scientific Electronic Library Online

 
vol.17 número1Studies on the loss of gloss of shellac and polyurethane finishes exposed to UVDecay and termite resistance of particleboard manufactured from wood, bamboo and rice husk índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Maderas. Ciencia y tecnología

versión On-line ISSN 0718-221X

Resumen

NAFCHI, Hajar Reisi et al. Effects of nano-clay particles and oxidized polypropylene polymers on improvement of the thermal properties of wood plastic composite. Maderas, Cienc. tecnol. [online]. 2015, vol.17, n.1, pp.45-54.  Epub 15-Nov-2014. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2015005000005.

In this study, the effects of oxidized polypropylene, as a compatibilizer, and Nano-clay particles in improving the thermal properties of wood plastic composites are investigated. For this purpose, polypropylene polymer was oxidized in the vicinity of the air oxygen for 2 hours. Then, in order to produce the samples, Nano-clay particles at three levels (0%, 2% and 4%) were mixed with wood fibers, polypropylene polymer and the compatibilizer. Finally, the samples with thickness of 2mm and dimensions of 15×15cm were made by using hot press. For more precise investigation, the morphology of wood plastic composites was studied by using X-rays diffraction and electronic microscope images. Thermal properties of the composites were evaluated through thermal and differential analyses. The results of the thermal tests demonstrated that the addition of oxidized polypropylene and Nano-clay particles significantly improve the thermal properties of wood plastic composites. Furthermore, increment of Nano-clay particles content additionally improves thermal stability of the composites and also reduces the released heat amount during the thermal degradation. In addition, TEM images showed that the dispersion of Nano-clay particles in the composite has an intercalation structure. This subject also verified by the X-rays diffraction and it is an evidence of better thermal stability of the achieved wood plastic composites.

Palabras clave : Thermal properties; wood plastic composites; nano-clay; compatibilizer; oxidized polypropylene.