SciELO - Scientific Electronic Library Online

 
vol.17 número2Utilization of temperature kinetics as a method to predict treatment intensity and corresponding treated wood quality: Durability and mechanical properties of thermally modified woodLiquefied wood as a partial substitute of melamine-urea-formaldehyde and urea-formaldehyde resins índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Maderas. Ciencia y tecnología

versão On-line ISSN 0718-221X

Resumo

ABDOLZADEH, H; EBRAHIMI, Gh; LAYEGHI, M  e  GHASSEMIEH, M. Analytical and experimental studies on stress capacity with modified wood members under combined stresses. Maderas, Cienc. tecnol. [online]. 2015, vol.17, n.2, pp.263-276.  Epub 26-Fev-2015. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2015005000025.

The stress capacity of joints made of modified wood members under loading can be affected by design of joints and type of adhesive. Hence, these factors were addressed in this study by assessment of stress capacity variations in corner joints under diagonal applied compressive load induced combined stresses. The joints with mitered and butted design were constructed by application of epoxy and polyvinyl acetate (PVAc) adhesives from furfurylated wood samples with two weight percentage gains (WPGs), i.e., 20% as low level and 60% as high level. Results indicated that stress capacity in both corner joints was not significantly decreased with increasing polymerization of furfuryl alcohol (FA) in wood. Despite the high compression strength in mitered joint, the induced compression stresses were low in comparison with butted joint. The stress capacity in mitered joint bonded with epoxy adhesive enhanced with increasing the level of furfurylation. This was true for shear stress parallel to grain as well. Generally, it could be concluded that mitered joint made of furfurylated members and bonded with epoxy adhesive would be stronger than other corner joints.

Palavras-chave : Corner joint; dowel; epoxy adhesive; furfurylation; stress capacity.