SciELO - Scientific Electronic Library Online

 
vol.18 número2Strategic planning for community sustainability in model forests: Case study of the Yoro model forest, HondurasPerformance of copper azole treated softwoods exposed to marine borers índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Maderas. Ciencia y tecnología

versión On-line ISSN 0718-221X

Resumen

DOGU, Dilek et al. Microscopic investigation of defects in thermally compressed poplar wood panels. Maderas, Cienc. tecnol. [online]. 2016, vol.18, n.2, pp.337-348. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2016005000031.

The combined effects of temperature and compression on the microstructure of solid-wood panels produced by Aspen (Populus tremula) wood were evaluated. Thermal compression was applied on aspen wood to increase the density for improving its physical and mechanical properties. The solid wood panels with dimensions of 100 mm by 500 mm by 25 mm were hot-pressed by using a laboratory hot press at a temperature of either 150°C or 170°C and pressure of either 1MPa or 2 MPa, respectively, for 45 min. Changes in the microstructure were detected by using a light microscope. The microscopic investigations revealed that the wood exhibited much defects in the process conditions of 170ºC / 2 MPa, and the distribution of defects were not uniform in the growth rings of the wood specimens in the two treatment groups. All defects in cell structure were quite distinct in the beginning and the last parts of the growth rings and the largest damages occurred in the fibers and vessels for the two process conditions. The results indicate that growth ring structure, vessel porosity, and cell wall thickness have a strong effect on wood behavior in various process conditions.

Palabras clave : Cellular failure; poplar wood; thermally compressed wood; wood densification; wood microstructure.