SciELO - Scientific Electronic Library Online

 
vol.20 número1Parquet multicapa de Eucalyptus globulus y Quercus robur . resistencia al impacto para diversas tipologías de fabricaciónComparison of two kiln-drying schedules for turkish hazel ( Corylus colurna ) lumber of 5-cm thickness índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Maderas. Ciencia y tecnología

versión On-line ISSN 0718-221X

Resumen

HAJIHASSANI, Reza; MOHEBBY, Behbood; NAJAFI, Saeed Kazemi  y  NAVI, Parviz. Influence of combined hygro-thermo-mechanical treatment on technical characteristics of poplar wood. Maderas, Cienc. tecnol. [online]. 2018, vol.20, n.1, pp.117-128. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2018005011001.

Combined hygro-thermo-mechanical technique was adopted and used for densification of poplar wood instead of sole treatment. This technique is combination of two techniques of hygrothermal treatment and densification of wood. For treatment, poplar wood blocks were initially treated hygrothermally at temperatures of 130, 150 and 170°C for holding time of 20, 40 minutes. Afterwards, the densification process was carried out under a hot press (temperature 160°C for 20 minutes). For densification compression set was adjusted for 40 and 60 % based on the initial thickness (radial direction) of the blocks. The densified and non-densified wood blocks were tested for physical and mechanical properties as density, water absorption, thickness swelling, springback, bending strength, modulus of elasticity as well as shear strength parallel to grain. Results revealed that wood properties were enhanced due to the combined hygro-thermo-mechanical -treatment. According to the results, wood density was increased due to the combined hygro-thermo-mechanical -treatment significantly. The treatment improved the dimensional stability of the densified samples. It was also found that the combined hygro-thermo-mechanical -treatment could significantly improve mechanical properties and also reduce the springback in the densified poplar wood.

Palabras clave : Compression set; hygrothermal treatment; mechanical properties; physical properties; Populus deltoides; wood densification.