SciELO - Scientific Electronic Library Online

 
vol.20 número3Plant essential oils for environment-friendly protection of wood objects against fungiArtificial neural networks to estimate the physical-mechanical properties of amazon second cutting cycle wood índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Maderas. Ciencia y tecnología

versión On-line ISSN 0718-221X

Resumen

HEIN, Paulo Ricardo Gherardi  y  BRANCHERIAU, Loïc. Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens. Maderas, Cienc. tecnol. [online]. 2018, vol.20, n.3, pp.333-342. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2018005003401.

Comparison between flexural wood strength values obtained from three-point and four-point bending tests in wood were only reported in few previous works, but remains unclear. Thus, the aim of this study was to determine the relationship between wood strength (MOR) obtained by 4-point and 3-point bending tests in Eucalyptus. Two or three specimens were cut from the same scantling (thus considered as twin) and submitted to flexural vibration tests. Then 190 wood specimens were tested by 4-point bending tests and 138 twin specimens were submitted to 3-point bending tests. Wood strength determined from 3-point bending test presented significantly higher mean value (76,8 MPa) than that from 4-point bending test (73 MPa). A linear regression for converting MOR from 3-point to 4-point bending test was proposed for these Eucalyptus specimens: MOR4p = 0,889 × MOR3p + 5,14 in MPa (R²=0,74). The correlation of MOR in 3-point bending with density was higher (R²=0,57) than in 4-point bending (R²=0,45). The correlations between dynamic elastic moduli and moduli of rupture were similar (circa R²=0,57 for MOR3p and R²=0,65 for MOR4p).

Palabras clave : Acoustic vibration; density; Eucalyptus grandis; static bending test; stiffness; strength.