J. Chil. Chem. Soc, 54, N° 1 (2009); págs: 23-27





Department of Chemistry, University of Calicut, Calicut University. P.O.,Kerala, India 673 635, Tel: +91 4942401144 *413.Fax: +91 4942400269. e-mail:


Chemically modified styrene butadiene rubber (SBR) with nitro and chloro functionalities are prepared by the nitromercuration reaction of SBR through a phase transfer catalyst. Activation energy for this chemical reaction calculated from the time temperature data on the chemical reaction by the measurement of percentage of chlorine indicated that the reaction proceeded according to fist order kinetics. The chemical modification is characterized by FTIR, UV, NMR studies reveal the attachment functional group such as nitro and chloro group to the double bond of butadiene moiety. The glass transition temperature of the functionalized SBR is analyzed using differential scarming calorimetry. Thermogravimetric analysis (TGA) of the modified SBR is investigated in orderto study the basic decomposition pattern and thermal stability of the materials. Chemical modification of SBR is accompanied by a reduction of double bond which imparts excellent tensile strength. The fíame resistances of the modified samples are analyzed by the limiting oxygenindex value (LOI) and the result of the studies show that as the level modification increases the tendency of ealstomeric material to burn decreases.

Keywords: Styrene butadiene rubber, nitromercuration, activation energy, glass transition, thermal, flammability, mechanical properties


The producers of general purpose synthetic rubbers have put a great deal of effort into the equipping of such rubbers with chemically functional groups along the polymer backbone chains. The purpose has been manifold, ranging from the improvement of green strength and tack to the provisión of sites for novel forms of crosslinking, grafting, antioxidant activity and even pharmacological properties. Usually a route to such functionalisation is to incorpórate small amounts of monomer carrying desired group in the polymerization process 1-6. However, polymerization with different functional groups will be expensive and therefore must be used only cheap reagent can be used for macro modification on elsatomers with quite new physical properties.

Synthetic rubber have made a great contribution to many industries, almost all are combustible in air. SBR is one of the elastomer which is widely used in tire industry and in underground coal mining, carpet underlay and car floor mats among other uses7,8. However, it has poor green strength and poor resistance against thermo oxidative degradation. Green strength which is cohesiveness in stretched uncured rubber compound is of great importance especially in the processing of tires. Many attempts have been carried out to increase the green strength of SBR and also to improve its oxidative and oil resistance. One attempt to increase the green strength is by the introduction of carbonyl during polymerization9. Another method is by introduction of tertiary amine containing monomers during polymerization followed by reaction with dihalides to form a small number of labile croslinks10,11. The technique of anionic polymerization using modified alkyl lithium initiators has been used to prepare high vinyl SBR12,13. Great attention has been paid to modifying SBR's combustión characteristics. Several approaches were made to decrease the tendency of elastomeric material to burn14,17.

Resistance to thermo-oxidative degradation is another important criteria to be satisfied for rubber producís used in outdoor applications ls. It is well known that the degradation of rubber is due to its reaction with molecular oxygen. This reaction can be suppressed by reducing the double bonds, or by introduction of functional groups that can deactivate the double bonds. The introduction of polar groups also brings about enhancement in resistance to oil, ozone, fíame and solvents. Particular attention will be focused to develop easily functionalisable smart polymers with optoelectronic properties by introducing functional group like azo and nitro group in the polymer chain by removing the easily labile mercuric chloride. Thus, this paper describes:(a) synthesis and kinetics of functional groups containing SBR (b) characterization of modified SBR using spectroscopic technique such as Fourier Transform Infrared Spectroscopy (FTIR), Fourier Transform Nuclear Magnetic Spectroscopy (FTNMR) and UV spectroscopy (c) glass transition temperature and thermal stability (d) fíame resistance and tensile strength of the modified SBR.



Styrene butadiene rubber (Synaprene 1502) has been obtained from Synthetics and Chemicals Ltd., Bareilly, U.P., India. Toluene, mercuric chloride, sodium nitrite, tetra butyl ammonium bromide, isopropyl alcohol are of reagent grade and supplied by Merck India Ltd., Mumbai.

IR spectra of samples are recorded with a Jasco Model No. 4100 Fourier transform infrared spectrophotometer, using thin film of polymer. UV spectra of the samples are recorded with a UV-550 spectrophotometer. 1HNMR spectrum of SBR and modified SBR are recorded on a Brucker, Fton MR 250 MHz spectrophotometer. Differential scarming calorimetry (DSC) analysis has performed on a Perkin Elmer 7 series differential scanning calorimeter at a heating rate of 5°C/min. TGA is carried out with a Shimadzu-50 thermogravimetric analyzer at a heating rate of 10°C/min in a dry nitrogen atmosphere.

The fíame resistance is measured with a Stanton Redcroft FTA flammability unit according to ASTM D 2863-77. Tensile strength of the unvulcanized sample is determined according to ASTM D 412-92 using dumbbell specimens. The test specimens are punched out from the sheet using C-type die. The thickness of the specimen within the gage length of the test specimen is measured using dial gage accuracy. OOlmm. The specimen are test on a 'Tinius OLSEM' -H-10K series instrument at a temperature of 25 ±2 °C and crosshead speed of 500mm/min.

Preparation of Nitromercurated styrene butadiene rubber (NSBR)

Addition of different functional group (NO2 and HgCl) group to SBR has been carried out by nitromercuration using phase transfer catalyst, tetra butyl ammonium bromide according to the method19 and later developed by Chein et al.20. SBR is dissolved in toluene, the phase transfer catalyst is added to this and the mixture is allowed to stir. To this mercuric chloride added followed by sodium nitrite. The reaction product is separated from the solution at a regular interval and washed with hot water and cold water, until free of chlorine. The product then coagulated with isopropyl alcohol and reprecipitated from toluene solution. The modification is monitored by the determination of nitrogen content by Kjeldahl method and chlorine percentage at different times using the method of chemical analysis. The reduction in double with different stages of chemical modification is carried out through determination of iodine value. The concentration of reagents, the temperature and time of reaction are given in Table 1.


Effect of time and temperatura on chemical modification in SBR

The percentages of chlorine versus time at different temperatures are given in Figure 1. The nitromercuration is fast in the initial stages but decreases at later stages of the reaction. The rate of reaction almost levéis off after lOh of reaction. The rate of reaction and the chlorine content increases with the temperature of the reaction. As far as the initial stage of the reaction is concerned, the reaction is extremely fast at 80°C.

Figure 2 shows the change in percentage of chlorine log (cα-ct) versus time, where cα in the maximum chlorine percentage obtained at the particular temperature and c is the percentage of chlorine at any time t. Linearity of the plot shows that the modification reaction proceeds according to first order kinetics. Rate constants (k) of the reaction calculated are 16.71 x 10-2 S-1, 17.97 x 10-2 S-1 and 21.98 x 10-2 S-1 at 30, 60 and 80°C respectively. The activation energy of the reaction calculated from the linear plot of log K versus 1/T (where K is the rate constant and T is the temperature in K) is found to be 104.8 kJ/mol.

Nitrogen content of chemically modified SBR

The percentage of nitrogen content in the modified SBR's is given in the Table 2. As far as the 2 hour reaction concerned there is a slight change in the eoneentration of nitrogen with increase in temperature. When the reaction reaches to four hours there is a sharp increase in the eoneentration of nitrogen content. Among the three reaction conditions 80°C samples exhibit the maximum eoneentration of nitrogen content. This clearly indicates thaton itromercuration reaction increases with increasing the time of reaction.

Iodine value of modified SBR at different time and temperature

The iodine value of the nitromercurated SBR's are given in the Table 3. It is observed from the table that as the reaction increases two hour, there is a small change in the iodine value with increase in temperature, where as the reaction proceeds after two hours shows a sharp decrease in iodine value. Among the three reaction conditions 80°C samples exhibit maximum decrease in iodine value. This clearly indicates thaton itromercuration reaction becomes more prominent at 4 hours, which leads to a greater reduction in double bond.

Characterization of modified SBR

FTIR characterization

FTIR spectra of SBR and modified SBR are given in Figure 3. It is apparent that the presence of C-H stretching (2930 and 2944 cm-1) CH2 in plañe deformation (1448 cm-1), -CH2 wagging motion (1376 cm-1) and trans C=C stretching (1000 cm-1). Typical styrene absorption oceurs at 750 cm-1 and 963 cm-1 (C-H out of plañe deformation of vinyl), nitromercurated samples shows the presence of chlorination band: C-Cl stretching (679 cm-1)21. Furthermore, there appears a new absorption peaks at 1640 cm-1 is due to antisymmetric NO stretch. Otherwise with increase in the duration of chemical reaction, there is a progressive reduction in the double bond eoneentration and corresponding increase in the eoneentration of C-Cl and NO2 bands, whereas the styrene eoneentration remains almost unchanged. Henee it can be inferred that it is the double bond 22 of butadiene that take part in the chemical modification. Therefore the chemical modification with increase in temperature leads to an increase in polarity in SBR due to the creation of C-Cl and N=0 groups. The proposed reaction is shown in Scheme 1.

UV spectroscopy

UV spectra of SBR and modified SBR (NSBR) with different chlorine content are shown in the Figure 4. It is clear that as temperature is increased, a hypsochromic shift occurs that is, a shift to higher energy or shorter wavelength. The hypsochromic shift is due to the decrease in the extent of double bonds.

FT 1H NMR Characterization

The 1H NMR spectra recorded for 3 and 6 % chlorine containing modified SBR are shown in Figure 5. The singlet at 7.3-7 ppm corresponds to the hydrogen is due to the symmetric aromatic proton . The two singlet at 2 and 1.4 ppm each corresponding to a single proton are due to the unsaturated methine hydrogen (-CH=) of butadiene moiety. The triplet at the región 1.4 to 1.9 ppm is due to the proton of-CH-C1. The singlet peak obtained at 0.9 ppm in SBR is due to the presence of tertiary hydrogen atom. Evidence showing addition reaction occurring is provided by the gradual decrease in the peak of (=CH—) and the increase in intensity of the extra peak at 2.3 ppm, due to proton of NO2 attached carbón atom. Thus the NMR spectrum confirms the formation of NO2 and Cl group in SBR.

Differential scanning calorimetry

Figure 6 demonstrated the DSC thermograms of SBR (1) and nitromercurated SBR with 3% (2) 6 % (3) and 9% chlorine content. The thermal transition at -58°C is the glass transition temperature (Tg) of the SBR. The overall appearance of the thermograms of nitromercurated samples (curve 2 & 3) is similar to the case of unmodified polymer. However there is a shift in the Tg occurs to the right as the level of mtromercuration increases. Modified SBR with 3% Cl shows a clear thermal transition at —56°C whereas 6% Cl containing polymer shows the thermal transition at —54°C. This observation reveals that as the level of nitromercuration increases Tg decreases. The lower Tg on nitromercuration indicates flexibility of the chain due to replacement of the rigid double bonds in the backbone of freely rotating single bonds.

The results obtained above are different from those obtained from the modified SBR with 9% chlorine (curve 4). It is obvious from the figure that in addition to the Tg of SBR signal at —54°C, there appears an endothermic peak at around —25°C. This indicates that during nitromercuration, there are structural changes, which can lead to crystallization at low temperature 23. As the modification proceeds, greater amount of Cl and NO2 groups are incorporated into butadiene units leading to increased polar interaction. The presence of specific groups which produce strong intermolecular bonds is one of the contributing factors for the development of low temperature crystallization24.

Thermogravimetric analysis

The thermograms of SBR and modified SBR's are given in the Figure 7. pure SBR shows single-stage decomposition at a temperature of initiation of 414°C. At low level of modification (curve 2 ) the therogarvimetric analysis curve of the modified SBR is similar to the unmodified SBR. Since under these conditions thermal degradation not yet started. On the contrary, at higher level of modification the mechanism of thermal degradation is very different. The modified polymer exhibits a two-stage degradation mechanism (curve 4 & 5). The first decomposition begins at 210 °C and second at 414 °C. The weight loss in the first stage of decomposition is due to the chlorine and NO2 group attached to the main chain of butadiene moiety and second is attributed to the degradation of the polyene residue.

The time taken for a 50% weight drop for SBR and modified SBR are presented in the Table 4. It is apparent from the table that the difference in thermal stability between the nitromercurated polymer is due to the difference in viscosity of the polymer, which affects the diffusion rate of volatile degradation product within the sample and partly due to the difference in the level of modification

Flammability behaviour

The limiting oxygenindex (LOI) (which is a direct measure of the fíame resistance of the materials) of pure SBR, and modified SBR are shown in the Figure 8. When the chlorine and nitrogen containing elastomers are ignited, they could exhibit an intumescence effect, due to which the char formed thermally insulates the polymer from the fíame and thus inhibits combustión. It is clear from the figure that modified SBR shows better fíame resistance than that of unmodified SBR. Moreover, the LOI value increases with increasing the level of chemical modifiaction. Substances with LOI value above 20.8 are classified as relatively safe while substances with LOI less than 20.8, which continue to burn in oxygen deficient air, are not safe as building material 25. Thus, modified SBR can be recommended as a substitute for building materials because these materials will be self-extinguishing even if ignited.

Tensile Strength

The tensile strength of the SBR and nitromercurated SBR (3 , 6 and 9 %chlorine) are given in Table 5. The tensile strength and maximum elongation of the samples increases progressively as the level of nitromercuration increases. It also reveals that the tensile strength of modified SBR is much more times greater than that of pure SBR. The excellent tensile strength to the modified SBR is due to a series of inter and intramolecular interaction such as hydrogen bonding, co-ordinate bond formation between the group such as nitro, mercuric, chloro and double bond etc.,


Chemical modification of SBR is carried out through nitromercuration by the addition of sodium nitrite and mercuric chloride using phase transfer catalyst. The activation energy of the chemical reaction is calculated from the time-temperature data on the chemical reaction by the measurement of the percentage of chlorine indicated that the reaction proceeded according to first-order kinetics. The percentage of nitrogen calculated using Kjeldahl method also shows a gradual increase in nitrogen content with time and temperature. The iodine value calculated shows a steady decrease in double bond concentration. The chemical modification is characterized by FTIR, UV and NMR spectroscopic studies. These studies revealedthe attachment of chlorine and NO2 to the double bond of butadiene. The glass transition temperature of the modified SBR is studied using DSC As the level of modification increases Tg decreases. The basic decomposition pattern and thermal stability of the samples are carried out using TGA. The fíame resistances of the chemically modified samples are analyzed and find that as the level modification increases the tendency of ealstomeric material to burn decreases. Chemical modification imparts excellent green strength to SBR which is almost several times greater than that of pure SBR. Studies on introducing other functionalisable smart polymers with optoelectronic properties in the polymer chain are underway.



1. J. C. Brosse, I. Campistron, D. Derouet, A. El. Hamdaoui, S. Houdayer, D. Reyx, S. Ritoit-Gillier, J. Appl. Polym. Sci. 78,1461, (2000)        [ Links ]

2. S. Yamashita, K. Kodama, Y. Ikeda, S. Kohjiya, J. Polym. Sci. Part A. Polym. Chem. 31, 2437, (1993)        [ Links ]

3. A. Rouilly, L. Rigal, G. G. Gilbert, Polymer 45, 7813, (2004)        [ Links ]

4. D. Derouet, Q. N. Tran, H. H Thuc, Eur. Polym. J. 43, 1806, (2007)        [ Links ]

5. A.F. Halasa, J.M. Massie, R. J. Ceresa The chemical modification of polymers, Science and Technology of Rubber, 3th edn., 2005        [ Links ]

6. J. Tyczkowski, I, Tyczkowski, B. Wozniak, Surface & Coatings Tech. 174, 849, (2003)        [ Links ]

7. M. H. Zhou, W.J. Cho, J. Appl. Polym. Sci. 89, 1818, (2003)        [ Links ]

8. J. Peng, Encyclopedia Chem Process 1,2871, 2005        [ Links ]

9. N. T. McManus, L.G. Rempel, Polym. Review 35. 239, (1995)        [ Links ]

10. C. M. Leir C. M. J. E. Stark, J. Appl. Polym. Sci. 38,1535, (1989)        [ Links ]

11. X. Chen, E. Ruckenstein, J. Polym. Sci. Part A: Polym Chem. 38, 1662, (2000)        [ Links ]

12. A. A.Yakubovich, B.I. Nakhmanovich, G. I. Litvinenko, Polymer 43, 7093,(2002)        [ Links ]

13. A. F. Halasa, B. Hsu, C. Jasiunas, Polymer 46, 4166, (2005)        [ Links ]

14. R.E. Lyon, L. Speitel, R.N. Walters, S. Crowley, Fire Mater. 27, 195, (2003)        [ Links ]

15. M. T. Ramesan, R. Alex, J. Appl. Polym. Sci. 68, 153, (1998)        [ Links ]

16. W. Jincheng, C. Yuehui, J. Elast. Plast. 39, 33, (2007)        [ Links ]

17. K. T. Varughese, P.P. De, S.K. De, J. Fire Sc. 7, 94, (1989)        [ Links ]

18. O. Zhou, W. Yang, Q. Wu,B. Yang, H. Jinman, J. Shen, Eur. Polym. J. 36, 1735, (2000)        [ Links ]

19. E. J. Corey H. Estreicher, J. Amer. Chem. Soc. 100, 6294 (1978)        [ Links ]

20. J. C. W. Chien, T. Kohara, C. P. Lillya, T. Sarubbi, B. H. Su, R.S. Miller, J. Polym. Sci. Polym. Chem. Edn. 18, 2723, (1980)        [ Links ]

21. S. A. Liebman, B.J. Gudzinowicz, Anal. Chem. 33, 931, (1961)        [ Links ]

22. H. Mayr, U.W. Heigl, Angew. Chem. Int. Ed. Engl. 24, 579, (1985)        [ Links ]

23. M. T. Ramesan, R. Alex, Kautsch. Gummi Kunstst. 10, 596, (2000)        [ Links ]

24. R. Stadler, J. Burgert, Makromol. Chem. 187, 1681, (1986)        [ Links ]

25. M. T. Ramesan, J. Polym. Res. 11, 333, (2004).        [ Links ]


(Received 26 February 2008 - Accepted 4 November 2008)

Creative Commons License Todo el contenido de esta revista, excepto dónde está identificado, está bajo una Licencia Creative Commons